Микроструктура и свойства сплава Al–Y–Er–Zr–Sc с примесями Fe и Si
| Τίτλος: | Микроструктура и свойства сплава Al–Y–Er–Zr–Sc с примесями Fe и Si |
|---|---|
| Συγγραφείς: | Barkov, R. Yu., Mochugovskiy, A. G., Yakovtseva, O. A., Pozdniakov, A. V. |
| Στοιχεία εκδότη: | Издательство Уральского университета, 2021. |
| Έτος έκδοσης: | 2021 |
| Θεματικοί όροι: | РЕДКОЗЕМЕЛЬНЫЕ МЕТАЛЛЫ РЕКРИСТАЛЛИЗАЦИЯ, ALUMINUM ALLOYS, МИКРОСТРУКТУРА, RARE EARTH METALS, АЛЮМИНИЕВЫЕ СПЛАВЫ, RECRYSTALLIZATION, МЕХАНИЧЕСКИЕ СВОЙСТВА, MICROSTRUCTURE, MECHANICAL PROPERTIES |
| Περιγραφή: | The influence of silicon and iron impurities on the structure, phase composition and mechanical properties of the alloy Al–0,2Y–0,3 Er–0,2Zr–0,05 Sc was investigated. In the alloy Al–Y–Er–Zr–0,05Sc (0,15 % (Fe and Si)), the presence of phases formed by impurities of iron and silicon was noted, there was an increased concentration of zirconium, erbium and yttrium in these phases, whereas for the alloy Al–Y–Er–Zr–0.05Sc (0,01 % (Fe and Si)), the formation of such phases was not observed. Исследовано влияние примесей кремния и железа на структуру, фазовый состав и механические свойства сплава Al–0,2Y–0,3Er–0,2Zr–0,05Sc. В сплаве Al–Y–Er–Zr–0,05Sc (0,15 % (Fe и Si)) отмечено наличие фаз, образованных примесями железа и кремния, наблюдается повышенная концентрация циркония, эрбия и иттрия в этих фазах, тогда как для сплава Al–Y–Er–Zr–0,05Sc (0,01 % (Fe и Si)) образование подобных фаз отмечено не было. |
| Τύπος εγγράφου: | Conference object |
| Περιγραφή αρχείου: | application/pdf |
| Γλώσσα: | Russian |
| Σύνδεσμος πρόσβασης: | http://elar.urfu.ru/handle/10995/97103 |
| Αριθμός Καταχώρησης: | edsair.od.......917..0a6ba19320cfd38a0b9f5ad6dbae6180 |
| Βάση Δεδομένων: | OpenAIRE |
| Η περιγραφή δεν είναι διαθέσιμη |