THE STUDY OF GUANIL UREA SULFATE AS A MODIFIER OF FIBREBOARD
| Τίτλος: | THE STUDY OF GUANIL UREA SULFATE AS A MODIFIER OF FIBREBOARD |
|---|---|
| Συγγραφείς: | Антон (Anton) Станиславович (Stanislavovich) Мазур (Mazur), Даниил (Daniil) Валерьевич (Valer'evich) Иванов (Ivanov), Адольф (Adol'f) Ануфриевич (Anufrievich) Леонович (Leonovich) |
| Πηγή: | chemistry of plant raw material; No 1 (2019); 277-285 Химия растительного сырья; № 1 (2019); 277-285 |
| Στοιχεία εκδότη: | Altai State University, 2019. |
| Έτος έκδοσης: | 2019 |
| Θεματικοί όροι: | MDF, дициандиамид, guanylurea sulfate, сульфат гуанилмочевины, cyanoguanidine, карбамидоформальдегидные смолы, 01 natural sciences, 0104 chemical sciences, формальдегид, acceptors of formaldehyde, акцепторы формальдегида, formaldehyde, токсичность древесных плит, toxicity of wood boards |
| Περιγραφή: | Fiberboards are producing of vegetable raw materials and urea-formaldehyde glues. The necessity to bind formaldehyde led to the search for modifiers that are capable to reduce the toxicity of wood boards without impairment of their physico-mechanical properties. It was researched how guanylurea sulfate influences on some process, which are occur during the formation of wood boards. The salts were synthesized at molar ratios of cyanoguanidine : sulfuric acid from 1 : 0.1 to 1 : 0.5 and their effects on the technological parameters of the glue were investigated. It was found that in combination with the urea-formaldehyde resin guanylurea sulfate sworn GUS-0.5 synthesized at a 1 : 0.5 molar ratio is most suitable as it accelerates hardening of the resin without negative influence on other standard parameters. Physicochemical tests and 13C solid-state NMR spectroscopy have shown that upon injection into the glue GUS-0.5 reacts with the functional groups of the urea-formaldehyde oligomer while embedding into the structure of the curing resin. At temperatures of hot pressing of wood boards in case of injection into the composition separately from the glue GUS-0.5 is subject to thermal transformations with the formation of ammonia. It’s shown that the properties of fiberboards depend on the method of injection of the modifier into the composition. To effectively reduce toxicity without impairment of their physico-mechanical properties should be used a combined method of using the modifier when one half is injected into the glue and the other half separately. |
| Τύπος εγγράφου: | Article Other literature type |
| Περιγραφή αρχείου: | application/pdf |
| ISSN: | 1029-5143 1029-5151 |
| DOI: | 10.14258/jcprm.2019014181 |
| Σύνδεσμος πρόσβασης: | http://journal.asu.ru/cw/article/download/4181/4121 http://journal.asu.ru/cw/article/view/4181 http://journal.asu.ru/cw/article/download/4181/4121 http://journal.asu.ru/cw/article/view/4181 |
| Rights: | CC BY NC ND CC BY |
| Αριθμός Καταχώρησης: | edsair.doi.dedup.....9cd67753a4d8ce6d1536d1ca87652eb2 |
| Βάση Δεδομένων: | OpenAIRE |
| ISSN: | 10295143 10295151 |
|---|---|
| DOI: | 10.14258/jcprm.2019014181 |