ТЕПЛОВЫЕ ИЗМЕНЕНИЯ АМОРФНЫХ СПЛАВОВ
| Τίτλος: | ТЕПЛОВЫЕ ИЗМЕНЕНИЯ АМОРФНЫХ СПЛАВОВ |
|---|---|
| Στοιχεία εκδότη: | ООО «Центр сопряженного мониторинга окружающей среды и природных ресурсов», 2020. |
| Έτος έκδοσης: | 2020 |
| Θεματικοί όροι: | металлическое стекло, metal glass, объемная доля, temperature, энергия Гиббса, crystallization rate, температура, химический потенциал, скорость кристаллизации, volume fraction, chemical potential, Gibbs energy, phase, фаза |
| Περιγραφή: | The calculation of temperature changes of sample volume is conducted at glass transition of melt and heating of metallic glass. It is shown that cooling of fusion with comparatively small (less than 0. 05 K/min) or large (more than 1200 K/min) speeds results in replacement of fracture on the indicated line on a smooth transition from the direct supercooled liquid to the line of glass. Heating of the metal glass with rates more than 500 K/min results in considerable expansion of temperature interval of phase transition. Проведен расчет температурных изменений объема образца при стекловании расплава и нагреве металлического стекла. Показано, что охлаждение расплава со сравнительно малыми (менее 0.05 K/min) или большими (более 1200 K/min) скоростями приводит к замене излома на указанной прямой на плавный переход от прямой переохлажденной жидкости к прямой стекла. Нагрев металлического стекла со скоростями более 500 K/min приводит к значительному расширению температурного интервала осуществления фазового перехода. Мониторинг. Наука и технологии, Выпуск 2 (44) 2020 |
| Τύπος εγγράφου: | Article |
| Γλώσσα: | Russian |
| DOI: | 10.25714/mnt.2020.44.012 |
| Αριθμός Καταχώρησης: | edsair.doi...........8648b6e0c41615b7024aba9c47512e7b |
| Βάση Δεδομένων: | OpenAIRE |
| DOI: | 10.25714/mnt.2020.44.012 |
|---|